Flexible plastic film

ABSTRACT

The present invention relates to a flexible plastic film, and more specifically to a flexible plastic film having excellent flexibility while exhibiting high hardness. According to the present invention, the flexible plastic film exhibits flexibility, bending property, high hardness, scratch resistance and high transparency, and hardly has a risk of damaging the film even in a state of being warped for a long period of time, and thereby can be usefully applied to flexible mobile devices, display devices, front face and display unit of various instrument panels, and the like.

CROSS-REFERENCE TO RELATED APPLICATION(S)

The present application is a 35 U.S.C. 371 National Phase Entry Application from PCT/KR2016/008571, filed Aug. 3, 2016, which claims the benefit of priority based on Korean Patent Application No. 10-2015-0109699 filed on Aug. 3, 2015, Korean Patent Application No. 10-2015-0130564 filed on Sep. 15, 2015, Korean Patent Application No. 10-2015-0160673 filed on Nov. 16, 2015, and Korean Patent Application No. 10-2016-0098076 filed on Aug. 1, 2016 with the Korean Intellectual Property Office, the disclosures of which are incorporated herein by reference in their entirety.

BACKGROUND OF THE INVENTION (a) Field of the Invention

The present invention relates to a flexible plastic film. More specifically, the present invention relates to a flexible plastic film having excellent flexibility while exhibiting high hardness.

(b) Description of the Related Art

Recently, with the development of mobile devices such as smartphones and tablet PCs, thinning and slimming of substrates for display are required. Glass or tempered glass is commonly used as a material having excellent mechanical properties on windows or front boards for displays of mobile devices. However, the glass causes the weight increase of the mobile devices due to its own weight, and has a problem of breakage due to an external impact.

Therefore, plastic resin is being studied as a substitute for glass. The plastic resin composition is lightweight but hardly has a risk of cracking and thus are suitable for the trend of pursuing lighter mobile devices. In particular, in order to implement a film having high hardness and abrasion resistance properties, a composition for coating a hard coating layer made of a plastic resin onto a support substrate has been proposed.

As a method of improving the surface hardness of the hard coating layer, a method of increasing the thickness of the hard coating layer can be considered. In order to ensure the surface hardness enough to replace the glass, it is necessary to implement a thickness of a certain hard coating layer. However, as the thickness of the hard coating layer is increased, the surface hardness may be increased but the occurrence of wrinkles and curls are increased due to curing shrinkage of the hard coating layer, and at the same time cracking and peeling of the coat layer are likely to occur. Therefore, the practical application of this method is not easy.

Korean Patent Laid-Open Publication No. 2010-0041992 discloses a plastic film composition using a binder resin containing an ultraviolet-curable polyurethane acrylate-based oligomer and eliminating monomers. However, the plastic film disclosed above has insufficient strength to replace a glass panel of a display with a pencil hardness of about 3H.

Meanwhile, a display in which a part of the display device is bent or flexibly warped for aesthetic and functional reasons has recently been attracting attention, and this tendency is noticeable particularly in mobile devices such as smartphones and tablet PCs. However, since glass is not suitable for use as a cover plate for protecting such a flexible display, it needs to be replaced with a plastic resin or the like. However, for that purpose, it is not easy to produce a thin film having sufficient flexibility while exhibiting a glass level of high hardness.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a flexible plastic film having excellent flexibility and bending stability while exhibiting high hardness.

In order to achieve the above object, the present provides a flexible plastic film comprising:

a support substrate; and an ultraviolet curable coating layer formed on at least one surface of the support substrate,

wherein the film exhibits a pencil hardness of 6 H or more under a load of 750 g, and

when placing the film at an interval of 4 mm in the middle of the film, allowing the film to stand while both sides of the film being folded at 90 degrees toward the bottom surface at room temperature, and then spreading the film on a flat bottom surface, a height lifted from the bottom surface is 0.5 mm or less.

The flexible plastic film according to the present invention exhibits flexibility, bending property, high hardness, scratch resistance and high transparency, and hardly has a risk of damaging the film even in repetitive, continuous bending or long-time folding state. Therefore, the plastic film can be usefully applied to bendable, flexible, rollable or foldable mobile devices, display devices, front face and display unit of various instrument panels, and the like.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a view schematically showing a method for performing a bending stability test of a film according to one embodiment of the present invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

The flexible plastic film of the present invention comprises: a support substrate; and an ultraviolet curable coating layer formed on at least one surface of the support substrate, wherein the film exhibits a pencil hardness of 6 H or more under a load of 750 g, and when placing the film at an interval of 4 mm in the middle of the film, allowing the film to stand while both sides of the film being folded at 90 degrees toward the bottom surface at room temperature, and then spreading the film on a flat bottom surface, a height lifted from the bottom surface is 0.5 mm or less.

In the present invention, the terms such as first, second, etc. are used to describe various components, and the terms are used only for the purpose of distinguishing one component from another component.

Moreover, the terminology used herein is for the purpose of describing exemplary embodiments only and is not intended to limit the present invention. The singular expression includes plural expressions unless the context clearly indicates otherwise. It will be understood that the terms such as “comprise,” “include,” “have,” etc. as used herein specify the presence of stated features, integers, steps, components, or combinations thereof but do not preclude the presence or addition of one or more other features, integers, steps, components, and/or combinations thereof.

As the present invention allows for various changes and numerous embodiments, particular embodiments will be illustrated and described in detail below. However, this is not intended to limit the present invention to particular modes of practice, and it is to be appreciated that all changes, equivalents, and substitutes that do not depart from the spirit and technical scope of the present invention are encompassed in the present invention.

The flexible plastic film of the present invention will be described in more detail below.

The flexible plastic film according to an embodiment of the present invention comprises: a support substrate; and an ultraviolet curable coating layer formed on at least one surface of the support substrate, wherein the film exhibits a pencil hardness of 6 H or more under a load of 750 g, and when placing the film at an interval of 4 mm in the middle of the film, allowing the film to stand while both sides of the film being folded at 90 degrees toward the bottom surface at room temperature, and then spreading the film on a flat bottom surface, a height lifted from the bottom surface is 0.5 mm or less.

In the present invention, “flexible” means a state having flexibility to such an extent that cracks of 3 mm or more in length do not occur when wound on a cylindrical mandrel with a diameter of 4 mm. Therefore, the flexible plastic film of the present invention can be applied to a cover film of a bendable, flexible, rollable, or foldable display or the like.

In mobile devices such as smartphones and tablet PCs and displays such as LCD, the form in which a part of the display device is bent or flexibly warped for aesthetic and functional reasons has recently been attracting attention, and this tendency is noticeable particularly in mobile devices. However, since glass is not suitable for use as a cover plate for protecting such a flexible display, it needs to be replaced with a plastic film including an ultraviolet curable or thermal curable resin or the like.

Among the cover plates made of a plastic resin, curved films forming a constant curvature and having a fixed form, or films having flexibility to the extent that can be bent by hand have been developed up to now, but it is inadequate to develop films having flexibility to such an extent that cracks do not occur even in repetitive bending or long-time folding state. Thinner films are advantageous for achieving flexibility but are relatively disadvantageous in terms of surface hardness. Therefore, it is not easy to provide a film having high flexibility and high hardness at the same time.

The present invention provides a plastic resin film including an ultraviolet curable coating layer which is implemented so as to simultaneously satisfy the physical property balance between flexibility and high hardness, and a flexible plastic film which exhibits high hardness and particularly hardly has a risk of damage of the film even by repetitive bending or folding operation, and thus can be applied to a bendable, flexible, rollable, or foldable mobile device, or a display device.

That is, the flexible plastic film according to the present invention comprises: a support substrate; and an ultraviolet curable coating layer formed on at least one surface of the support substrate, wherein the film exhibits a pencil hardness of 6 H or more under a load of 750 g, and when placing the film at an interval of 4 mm in the middle of the film, allowing the film to stand while both sides of the film being folded at 90 degrees toward the bottom surface at room temperature, and then spreading the film on a flat bottom surface, the film exhibits a bending stability to such an extent that a height lifted from the bottom surface is 0.5 mm or less.

FIG. 1 is a view schematically showing a method for measuring a bending stability property of a flexible plastic film according to one embodiment of the present invention.

Referring to FIG. 1, the film is placed so as to be horizontal with the bottom, and set so that the interval between the portions folded at a middle portion of the film is 4 mm. The film is allowed to stand at room temperature for a certain period of time, for example about 12 to about 72 hours, while both sides of the films being folded at 90 degrees toward the bottom surface. The film is spread on the flat bottom surface so that the folded portion goes downward. By the method of measuring the stability against bending after 1 hour, the stability against bending can be measured.

At this time, in order to maintain the distance between the folding portions constant, for example, the film is placed so as to be in contact with a rod having a diameter (R) of 4 mm, the remaining portion of the film is fixed, and the processes of folding and spreading both sides of the film around the rod can be performed. Further, the folded portion is not particularly limited as long as it is the inside of the film, and for convenience of measurement, the central portion of the film may be folded so that the remaining portions of the film excluding the folded portion are symmetrical.

In measuring such stability, the flexible plastic film of the present invention has a height lifted from the bottom surface of about 0.5 mm or less, or about 0.3 mm or less, or about 0.2 mm or less even after it is allowed to stand in a state of being folded for about 12 to about 72 hours, and it can be restored substantially to the original flat state.

Therefore, even in actual application conditions such as folding, rolling or warping for a long period of time, the possibility of occurrence of cracks or deformation of the film such as lifting, or of distortion of the film at the warped or folded portion is extremely low, and thus the flexible plastic film can be suitably applied for a cover plate of a flexible display.

Further, the flexible plastic film of the present invention can have a pencil hardness of 6 H or more or 7 H or more under a load of 750 g,

As mentioned above, thinning the thickness of the film is advantageous for realizing flexibility, but the surface hardness becomes relatively low. Therefore, it is not easy to provide a film having a high hardness simultaneously while having high flexibility. However, the flexible plastic film of the present invention achieved the bending stability of 12 hours or more the high hardness of 6H or more or 7H or more under a load of 750 g, by matching with the two conflicting physical properties.

That is, the present invention has been completed on the basis of that, when a plastic film has a structure including a support substrate and a coating layer formed on at least one surface of the support substrate and at the same time satisfies a pencil hardness of 6 H or more under a load of 750 g and physical properties that restore to the original flat state even after maintaining a bending or folding state for a predetermined time, it can be practically applied to bendable, flexible, rollable or foldable mobile device, display device, etc.

The flexible plastic film of the present invention which simultaneously satisfies these bending stability and surface hardness can be obtained by optimizing the support substrate and the ultraviolet curable coating layer (hereinafter, referred to as a coating layer) formed on the support substrate.

For example, in the flexible plastic film of the present invention, the support substrate on which the coating layer is formed is an optical transparent plastic resin having an elastic modulus of about 4 GPa or more as measured according to ASTM D882 and a thickness in the range of 20 to 200 μm so that it secures flexibility and hardness, and can be used without particularly limiting the method and material for producing the support substrate such as a stretched film or a non-stretched film.

Among the conditions of the support substrate, the elastic modulus may be about 4 GPa or more, or about 5 GPa or more, or about 5.5 GPa or more, or about 6 GPa or more, and the upper limit value may be about 9 GPa or less, or about 8 GPa or less, or about 7 GPa or less. If the elastic modulus is less than 4 GPa, sufficient hardness cannot be achieved, and if the elastic modulus exceeds 9 Gpa which is too high, it may be difficult to form a film having flexibility.

The thickness of the support substrate may be about 20 μm or more, or about 25 μm or more, or about 30 μm or more, and the upper limit value thereof may be about 200 μm or less, or about 150 μm or less, or about 100 or less, or about 60 μm or less. If the thickness of the support substrate is less than 20 μm, there is a possibility that breakage or curling occurs in the process of forming the coating layer, and it may be difficult to achieve high hardness. On the other hand, if the thickness exceeds 200 μm, the flexibility deteriorates and it may be difficult to form a flexible film.

From the viewpoint of ensuring the processibility for the flexible film and achieving the physical property balance between the high hardness and the flexibility as described above, a support substrate having an elastic modulus of 4 GPa or more and 9 GPa or less and a thickness in the range of 20 to 200 μm can be used.

More specifically, according to one embodiment of the present invention, the support substrate satisfies the above-described elastic modulus and thickness range, and for example, it may be a film including polyimide (PI), polyimideamide, polyetherimide (PEI), polyethyleneterephtalate (PET), polyethylenenaphthalate (PEN), polyetheretherketone (PEEK), cyclic olefin polymer (COP), polyacrylate (PAC), polymethylmethacrylate (PMMA), triacetylcellulose (TAC), and the like. The above support substrate may have a single layer or a multilayer structure including, if necessary, two or more substrates composed of the same as or different substances, and is not particularly limited.

Alternatively, according to one embodiment of the present invention, the support substrate may be a substrate comprising polyimide (PI).

Further, according to one embodiment of the present invention, the thickness ratio between the support substrate and the coating layer may be about 1:0.05 to about 1:1, or about 1:0.1 to about 1:0.8. When the thickness ratio between the support substrate and the coating layer is within the above range, a flexible plastic film exhibiting high hardness and flexibility can be formed more easily.

The flexible plastic film of the present invention includes an ultraviolet curable coating layer formed on at least one surface of the support substrate.

According to one embodiment of the present invention, the coating layer may be formed on both surfaces of the support substrate.

In the flexible plastic film of the present invention, the coating layer comprises a crosslinked copolymer of a 3- to 6-functional acrylate-based binder and a 7- to 20-functional urethane acrylate-based binder, and inorganic fine particles having a bimodal particle size distribution including a first inorganic fine particle group having d₅₀ of 20 to 35 nm and a second inorganic fine particle group having d₅₀ of 40 to 130 nm.

As used herein, the acrylate-based means not only acrylate but also methacrylate, or derivatives in which a substituents are introduced into acrylate or methacrylate.

The 3- to 6-functional acrylate-based binder is cross-linked with the 7- to 20-functional urethane acrylate-based binder to form a copolymer, and can impart high hardness to the coating layer formed after curing.

More specifically, the 3- to 6-functional acrylate-based binder may include trimethylolpropane triacrylate (TMPTA), trimethylolpropaneethoxy triacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA), pentaerythritol tetraacrylate (PETA), dipentaerythritol hexaacrylate (DPHA), and the like. The above-mentioned 3- to 6-functional acrylate-based binder may be used alone or in combination of different types.

According to one embodiment of the present invention, the 3- to 6-functional acrylate-based binder has a weight average molecular weight (Mw) ranging from about 200 to about 2,000 g/mol, or from about 200 to about 1,000 g/mol, or about 200 to about 500 g/mol.

According to one embodiment of the present invention, the 3- to 6-functional acrylate-based binder has an acrylate equivalent weight ranging from about 50 to about 300 g/mol, or from about 50 to about 200 g/mol, or from about 50 to about 150 g/mol.

When the weight average molecular weight and the acrylate equivalent weight of the 3- to 6-functional acrylate-based binder are respectively within the above-mentioned ranges, a coating layer having more optimized physical properties can be formed.

The 7- to 20-functional urethane acrylate-based binder is cross-linked with the 3- to 6-functional acrylate-based binder to form a copolymer, and may impart high hardness, flexibility and impact resistance to the coating layer formed after curing. The 7- to 20-functional urethane acrylate-based binder may be used alone or in combination of different types.

According to one embodiment of the present invention, the cross-linked copolymer may be one in which the 3- to 6-functional acrylate-based binder and the 7- to 20-functional urethane acrylate-based binder are cross-linked in a ratio of about 1:9 to about 5:5, preferably 1:9 to about 4:6, more preferably from about 1:9 to about 3.5:6.5. By including the cross-linked copolymer in which the 3- to 6-functional acrylate-based binder and the 7- to 20-functional urethane acrylate-based binder are cross-linked in the weight ratio described above, it can exhibit sufficient flexibility and at the same time achieve high hardness and good physical properties.

According to one embodiment of the present invention, the 7- to 20-functional urethane acrylate-based binder has a weight average molecular weight ranging from about 2,000 to about 8,000 g/mol, or from about 3,000 to about 6,000 g/mol, or from about 3,000 to about 5,000 g/mol which may be preferable for the optimization of the physical properties of the coating layer.

According to an embodiment of the present invention, the 7- to 20-functional urethane acrylate-based binder may have an acrylate equivalent weight ranging from about 200 to about 1,500 g/mol, or from about 200 to about 1,000 g/mol, or from about 300 to about 600 g/mol, or from about 300 to about 500 g/mol. If the acrylate equivalent weight of the 7- to 20-functional urethane acrylate-based binder is too high, the hardness of the coating layer may be insufficient, and if the equivalent weight is low, the hardness may be improved but the flexibility may be deteriorated. From the viewpoint of balance between high hardness and flexibility as described above, the above-mentioned equivalent weight range is preferable, and about 300 to about 500 g/mol may be most preferable.

When the weight average molecular weight and the acrylate equivalent weight of the 7- to 20-functional urethane acrylate-based binder are respectively within the ranges described above, coating layers having more optimized properties can be formed.

As the 7- to 20-functional urethane acrylate-based binder contains in the molecule at least 7 acrylate groups capable of performing a crosslinking polymerization by ultraviolet rays, it is advantageous for achieving high hardness of the coating layer. However, the higher the cross-linking density, it allows the curls to be easily generated and the adhesive force with the substrate is lowered, and so it is not suitable for forming a flexible film.

Meanwhile, the 7- to 20-functional urethane acrylate-based binder contained in the coating layer of the present invention includes at least 7 polyfunctional acrylate groups and at the same time has a urethane bond in the molecule, and thus is excellent in elasticity and flexibility. Accordingly, when it is cross-linked with a 3- to 6-functional acrylate-based binder at an appropriate weight ratio to form a copolymer, it serves to impart sufficient flexibility together with high hardness to the coating layer. The 7- to 20-functional urethane acrylate-based binder may contain 2 to 20 urethane bonds in one molecule.

As such, the coating layer according to one embodiment of the present invention includes a crosslinked copolymer in which the 3- to 6-functional acrylate-based binder and the 7 to 20-functional urethane acrylate-based binder are cross-linked to each other, thereby imparting high hardness and flexibility to the flexible plastic film. In particular, it has high stability against bending, rolling or folding, and thus it is possible to secure excellent flexibility and stability, which hardly has a risk of damaging the film even when repeatedly warped or folded for a long time.

The coating layer according to one embodiment of the present invention comprises inorganic fine particles having a bimodal particle size distribution including a first inorganic fine particle group having d₅₀ of 20 to 35 nm and a second inorganic fine particle group having d₅₀ of 40 to 130 nm. As described above, the coating layer of the present invention uses the inorganic fine particles exhibiting a bimodal particle size distribution including the first and second inorganic fine particle groups each having a specific range of d₅₀, thereby improving the hardness and flexibility of the coating layer simultaneously while maintaining the flexible property.

In the specification of the present invention, when a cumulative particle size distribution corresponding to particle sizes was measured using a laser light diffraction method (measurement method: size distribution by number is determined by using dynamic laser scattering, a solvent in which inorganic fine particles are dispersed, refractive index, viscosity, and dielectric constant of the inorganic fine particles, the equipment name: Malvern Zetasizer Nano-ZS 90), the particle size at the 10% cumulative is set to d₁₀, the particle size at the 50% cumulative to d₅₀, and the particle size at the 90% cumulative to d₉₀. The particle size distribution by the laser light diffraction method can show substantially the same distribution as that measured with SEM or TEM by diluting a dispersion liquid in which inorganic fine particles are dispersed in a solvent, or measured by analyzing the cross section of the coating layer containing the inorganic fine particles by SEM or TEM.

The first inorganic fine particle group having the small particle size range contributes to the improvement of the hardness, and the second inorganic fine particle group having the larger particle size range contributes to the improvement of bending property and flexibility. In this way, as other inorganic fine particle groups having different particle size ranges are mixed and used in addition to the cross-linked copolymer described above, it is possible to provide a coating layer in which the physical properties of hardness and flexibility are improved simultaneously.

As the first and second inorganic fine particle groups, for example, silica fine particles, aluminum oxide particles, titanium oxide particles, zinc oxide particles or the like may be each independently used.

According to one embodiment of the present invention, the d₅₀ of the first inorganic fine particle group may be 20 nm or more, or about 21 nm or more, 35 nm or less, 30 nm or less, or 25 nm or less, and the d₅₀ of the second inorganic fine particle group may be about 40 nm or more, or about 42 nm or more, or about 45 nm or more, and 130 nm or less, or 125 nm or less, or 120 nm or less.

According to one embodiment of the present invention, the first inorganic fine particle group may have d₁₀ of 10 to 19 nm, d₅₀ of 20 to 35 nm, and a d₉₀ of 25 to 40 nm. Further, the second inorganic fine particle group may have d₁₀ of 25 to 110 nm, d₅₀ of 40 to 130 nm, and d₉₀ of 60 to 150 nm.

According to one embodiment of the present invention, the content of the first inorganic fine particle group may be about 5 parts by weight or more, or about 10 parts by weight or more, or about 15 parts by weight or more, based on 100 parts by weight of the coating layer, in order to contribute to an improvement in high hardness. The content of the first inorganic fine particle group may be about 50 parts by weight or less, or about 45 parts by weight or less, or about 40 parts by weight or less, or about 35 parts by weight or less, in order to satisfy the flexibility. By including the first inorganic fine particle group within the weight range described above, it is possible to form a flexible plastic film having excellent physical properties simultaneously satisfying both high hardness and flexibility.

Further, according to one embodiment of the present invention, the content of the second inorganic fine particle group may be about 5 parts by weight or more, or about 10 parts by weight or more, or 15 parts by weight or more, based on 100 parts by weight of the entire coating layer, in order to contribute to an improvement in high hardness, and may be about 50 parts by weight or less, or about 45 parts by weight or less, or about 40 parts by weight or less, or about 35 parts by weight or less in order to satisfy flexibility. By including the second inorganic fine particle group within the weight range described above, it is possible to form a flexible plastic film having excellent physical properties simultaneously satisfying both high hardness and flexibility.

According to one embodiment of the present invention, the total content of the inorganic fine particles including the first and second inorganic fine particle groups may be about 25 parts by weight or more, or about 30 parts by weight or more, or about 35 parts by weight or more, based on 100 parts by weight of the entire coating layer, in order to contribute to an improvement in high hardness, and may be about 50 parts by weight or less, or about 45 parts by weight or less, or about 40 parts by weight or less in order to satisfy flexibility.

According to one embodiment of the present invention, the first and second inorganic fine particle groups may be the same or different and each independently surface-modified with any one or more silane coupling agents selected from the group consisting of (meth)acrylsilane, methacryloxysilane, vinylsilane, epoxysilane, and mercaptosilane.

Since the first and second inorganic fine particle groups surface-modified with the silane coupling agent as described above can react with the acrylate group of the binder, the adhesion to the substrate is high, they can be uniformly dispersed in the coating layer, and the hardness can be improved without deteriorating the flexibility of the coating layer, which are therefore more advantageous.

According to one embodiment of the present invention, the first and second inorganic fine particle groups may be present in the weight ratio of about 9:1 to about 3:7, or about 8:2 to about 4:6, or about 7:3 to about 5:5. By including the first and second inorganic fine particle groups within the weight ratio range described above, it is possible to form a flexible plastic film having excellent physical properties with enhanced high hardness and flexibility.

Meanwhile, the coating layer of the present invention may further include additives commonly used in the art, such as a surfactant, a UV absorber, a UV stabilizer, an anti-yellowing agent, a leveling agent, an antifouling agent, a dye for improving the color value, etc., in addition to the above-mentioned binder, inorganic fine particles, photoinitiator and organic solvent. Further, the content thereof is not particularly limited as it can be variously adjusted within the range that does not deteriorate the physical properties of the coating layer of the present invention. However, they may be contained in an amount of about 0.01 to 10 parts by weight based on about 100 parts by weight of the coating layer.

According to an embodiment of the present invention, for example, the coating layer may contain a surfactant as an additive, and the surfactant may be a mono- or bi-functional fluorine-based acrylate, a fluorine-based surfactant, or a silicon-based surfactant. In this case, the surfactant may be included in a form of being dispersed or crosslinked in the crosslinked copolymer.

Further, the additive may include a UV absorber, a UV stabilizer, and examples of the UV absorber include a benzophenone-based compound, a benzotriazole-based compound, a triazine-based compound and the like. Examples of the UV stabilizer include tetramethyl piperidine or the like.

The coating layer according to one embodiment of the present invention as described above may be formed by photo-curing a coating composition comprising a 3- to 6-functional acrylate-based binder, a 7- to 20-functional urethane acrylate-based binder, photoinitiator, inorganic fine particles having a bimodal particle size distribution including a first inorganic fine particle group having d₅₀ of 20 to 35 nm and a second inorganic fine particle group having d₅₀ of 40 to 130 nm, additives, and an organic solvent.

Examples of the photoinitiator may include 1-hydroxy-cyclohexyl-phenyl ketone, 2-hydroxy-2-methyl-1-phenyl-1-propanone, 2-hydroxy-1-[4-(2-hydroxyethoxy)phenyl]-2-methyl-1-propanone, methylbenzoylformate, α,α-dimethoxy-α-phenylacetophenone, 2-benzoyl-2-(dimethylamino)-1-[4-(4-morpholinyl)phenyl]-1-butanone, 2-methyl-1-[4-(methylthio) phenyl]-2-(4-morpholinyl)-1-propanone diphenyl(2,4,6-trimethylbenzoyl)-phosphine oxide, or bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide, and the like, but are not limited thereto. In addition, examples of commercially available products include Irgacure 184, Irgacure 500, Irgacure 651, Irgacure 369, Irgacure 907, Darocur 1173, Darocur MBF, Irgacure 819, Darocur TPO, Irgacure 907, Esacure KIP 100F, and the like. These photoinitiators can be used alone or in combination of two or more.

Examples of the organic solvent include alcohol based solvents such as methanol, ethanol, isopropyl alcohol and butanol; alkoxy alcohol based solvents such as 2-methoxyethanol, 2-ethoxyethanol and 1-methoxy-2-propanol; ketone based solvents such as acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl propyl ketone and cyclohexanone; ether based solvent such as propylene glycol monopropyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethyl glycol monoethyl ether, diethyl glycol monopropyl ether, diethyl glycol monobutyl ether and diethylene glycol-2-ethylhexyl ether; aromatic solvent such as benzene, toluene and xylene, and the like. These may be used alone or in combination.

The content of the organic solvent is not particularly limited since it can be variously adjusted within a range that does not deteriorate the physical properties of the coating composition, but it can included so that the weight ratio of the solid content:organic solvent is about 30:70 to about 99:1 based on the solid content of the components contained in the coating composition. When the organic solvent is within the above range, it can have appropriate fluidity and coating property.

The coating composition may be each sequentially coated onto the front and rear surfaces of the support substrate, or simultaneously coated onto both surfaces of the support substrate.

According to one embodiment of the present invention, the coating composition comprising the above-described components can be coated onto both surfaces of the support substrate and then photo-cured to form a coating layer, thereby obtaining the flexible plastic film of the present invention. Here, the method of coating the coating composition is not particularly limited as long as it can be used in the technical field to which the present technology belongs, and for example, a bar coating method, a knife coating method, a roll coating method, a blade coating method, a die coating method, a micro gravure coating method, a comma coating method, a slot die coating method, a lip coating method, a solution casting method, or the like can be used.

The coating layer may have a thickness of about 3 μm or more, for example about 3 to about 20 μm, or about 3 to about 15 μm, or about 3 to about 10 μm after being completely cured. According to the present invention, it is possible to provide a flexible plastic film having a high hardness when a coating layer having such a thickness is included.

According to one embodiment of the present invention, the flexible plastic film may further include at least one selected from a layer, a membrane, a film or the like such as a plastic resin film, a cohesive film, a release film, a conductive film, a conductive layer, a liquid crystal layer, a coating layer, a cured resin layer, a non-conductive film, a metal mesh layer or a patterned metal layer on the top surface of at least one coating layer or between the substrate film and the coating layer. For example, an antistatic layer having conductivity is first formed on a support substrate, and then a coating layer is formed thereon to provide an anti-static function, or a low refractive index layer is introduced on the coating layer to implement a low reflection function.

Further, the layer, membrane, film or the like may be in any form of a single layer, a double layer, or a laminate type. The layer, membrane, film or the like may be formed by laminating a freestanding film with an adhesive, a cohesive film, or the like, or may be laminated on the coating layer by a method such as coating, vapor deposition, sputtering, or the like, but the present invention is not limited thereto.

The flexible plastic film according to the present invention can be produced, for example, by the following method.

According to one embodiment of the present invention, the flexible plastic film can be formed by a two-step process of first coating and first photo-curing a first coating composition on one surface of a support substrate, and then second coating and second photo-curing the coating composition on the other surface, that is the back side of the support substrate. At this time, the first and second coating compositions are the same as the above-described coating composition, and each of them distinguishes the composition coated onto only one surface and the back surface.

In the case of forming the coating layer by this method, in the second photo-curing step, ultraviolet ray irradiation is performed not on the surface coated with the first coating composition but on the opposite surface, and thereby curls which may be generated due to curing shrinkage in the first photo-curing step can be cancelled out in opposite directions to obtain a flat flexible plastic film. Therefore, no additional flattening process is required.

However, the present invention is not limited thereto, and the curl balance can also be adjusted by forming the coating composition simultaneously on both surfaces of the support substrate and then curing the coating composition.

The flexible plastic film of the present invention exhibits excellent flexibility, bending property, high hardness, scratch resistance, high transparency, high durability and stability against bending, rolling or folding and thus can be used as a cover film of a next generation display having bendable, flexible, rollable or foldable properties, and the like.

For example, the flexible plastic film of the present invention can exhibit flexibility to such an extent that cracks do not occur when wound on a cylindrical mandrel with a diameter of 4 mm or 3 mm.

Further, the flexible plastic film of the present invention may have a pencil hardness of 6H or more, or 7H or more, under a load of 750 g.

In addition, the flexible plastic film can generate 2 or less scratches when steel wool #0000 is attached to a tip having a contact area of 2 cm×2 cm with respect to a plastic film in a friction tester and then the surface of the plastic film is reciprocated 400 times under a load of 500 g.

Further, the flexible plastic film of the present invention may have a light transmittance of 88.0% or more, or 90.0% or more, and a haze of 1.5% or less, 1.0% or less, or 0.5% or less.

The flexible plastic film of the present invention can be utilized in various fields. For example, the flexible plastic film of the present invention can be used as a flat-shaped as well as a curved, bendable, flexible, rollable or foldable-shaped mobile communication terminal, a touch panel of a smartphone or a tablet PC, and cover substrate or element substrate of various displays.

Hereinafter, the operation and effect of the invention will be described in more detail by way of concrete examples. However, these examples are merely presented for illustrative purposes only, and the scope of the invention is not determined thereby.

EXAMPLES Example 1

30 g of trimethylolpropane triacrylate (TMPTA) (manufactured by Cytec, Mw=296 g/mol, acrylate group equivalent weight=99 g/mol) as a trifunctional acrylate-based binder, 40 g of MU9800 (manufactured by Miwon, Mw=3500 g/mol, acrylate group equivalent weight=389 g/mol) as a 9-functional urethane acrylate-based binder, 30 g of MU9020 (manufactured by Miwon, Mw=4500 g/mol, acrylate group equivalent weight=450 g/mol) as a 10-functional urethane acrylate-based binder, 1 g of Irgacure 184 (manufactured by Ciba) as a photoinitiator, and 15 g of methyl ethyl ketone (MEK) were mixed to prepare an acrylate solution.

60 g of a solution in which a silica particle S1 (d₁₀=17 nm, d₅₀=22 nm, d₉₀=28 nm, surface-modified with methacrylate silane coupling agent) was dispersed in n-BA 3 (normal butyl acetate) in an amount of 50% by weight (hereinafter, referred to as S1 dispersion solution), and 50 g of a solution in which a silica particle S2 (d₁₀=29 nm, d₅₀=51 nm, d₉₀=74 nm, surface-modified with an acrylate silane coupling agent) was dispersed in MEK in an amount of 30% by weight (hereinafter, referred to as S2 dispersion solution) were mixed with the resulting acrylate solution to prepare a coating composition.

The coating composition was coated onto both surfaces of a polyimide substrate (size: 20 cm×30 cm, thickness: 35 μm) having an elastic modulus value of 6.0 GPa as measured according to ASTM D882 by a bar coating method, and photo-cured with a metal halide lamp having a wavelength of 290 to 320 nm to form a coating layer.

After the curing was completed, the thickness of the coating layer formed on both surfaces was 6 μm, respectively.

Example 2

The coating layer was formed in the same manner as in Example 1, except that the S2 dispersion solution was used in an amount of 83.3 g of and no additional methyl ethyl ketone solvent was contained.

Example 3

The coating layer was formed in the same manner as in Example 1, except that 25 g of methyl ethyl ketone was used, and 37.5 g of a solution in which a silica particle S3 (d₁₀=108 nm, d₅₀=119 nm, d₉₀=131 nm, surface-modified with an acrylate silane coupling agent) was dispersed in MEK in an amount of 40% by weight (hereinafter, referred to as S3 dispersion solution) was mixed instead of 50 g of the S2 dispersion solution to prepare a coating composition.

The subsequent steps were carried out in the same manner as in Example 1 to form a coating layer.

Example 4

20 g of TMPTA (manufactured by Cytec, Mw=296 g/mol, acrylate group equivalent weight=99 g/mol), 40 g of MU9800 (manufactured by Miwon, Mw=3500 g/mol, acrylate group equivalent weight=389 g/mol), 40 g of MU9020 (manufactured by Miwon, Mw=4500 g/mol, acrylate group equivalent weight=450 g/mol), 1 g of Irgacure 184 (manufactured by Ciba) as a photoinitiator and 12 g of methylethyl ketone (MEK) were mixed to prepare an acrylate solution.

60 g of the S1 dispersion solution and 75 g of the S3 dispersion solution were mixed with the resulting acrylate solution to prepare a coating composition.

The subsequent steps were carried out in the same manner as in Example 1 to form a coating layer.

Example 5

Except for using a polyimide substrate (size: 20 cm×30 cm, thickness: 35 m) having an elastic modulus value of 4.2 GPa as measured in accordance with ASTM D 882, the other steps were carried out in the same manner as in Example 1 to form a coating layer.

Example 6

Except for using a polyimide substrate (size: 20 cm×30 cm, thickness: 35 μm) having an elastic modulus value of 7.6 GPa as measured in accordance with ASTM D 882, the other steps were carried out in the same manner as in Example 1 to form a coating layer.

Example 7

30 g of TMPTA (manufactured by Cytec, Mw=296 g/mol, acrylate group equivalent weight=99 g/mol), 30 g of MU9020 (manufactured by Miwon, Mw=4500 g/mol, acrylate group equivalent weight=450 g/mol), 40 g of SC 2152 (manufactured by Miwon, Mw=20,000 g/mol, acrylate group equivalent weight=1,333 g/mol) as a 15-functional urethane acrylate-based binder, 1 g of Irgacure 184 (manufactured by Ciba) as a photoinitiator, and 42 g of methyl ethyl ketone (MEK) were mixed to prepare an acrylate solution.

60 g of the S1 dispersion solution and 83.3 g of the S2 dispersion solution were mixed with the resulting acrylate solution to prepare a coating composition.

The subsequent steps were carried out in the same manner as in Example 1 to form a coating layer.

Example 8

20 g of AZO particle dispersion CX-610M (manufactured by Nissan, solid content 60%), 10 g of dipentaerythritol pentaacrylate (DPHA), 0.5 g of Irgacure 184 (manufactured by Ciba) as a photoinitiator and 100 g of ethanol were mixed to prepare an antistatic layer composition.

The antistatic layer composition was coated on one surface of the polyimide substrate used in Example 1 and photo-cured to form an antistatic layer having a thickness of 1 μm and a surface resistance of 10⁹ Ω/sq.

The coating composition of Example 1 was coated onto the upper surface of the antistatic layer and the other surface of the substrate on which the antistatic layer was not formed, and photo-cured to form coating layers each having a thickness of 6 mm.

Example 9

First, a coating layer was formed on both surfaces of the polyimide substrate by the same process as in Example 1.

22 g of hollow silica dispersion Thrulya 4320 (manufactured by Catalysts & Chemicals Ltd., solid content 20%), 4 g of dipentaerythritol pentacrylate (DPHA), 0.5 g of photoinitiator Irgacure 184 (manufactured by Ciba), a fluorine-containing compound RS907 (manufactured by DIC, solid content 30%) were mixed to prepare a low refractive index layer composition.

The low refractive index layer composition was coated onto one surface of the coating layer and photo-cured to form a low refractive index layer having a thickness of 120 nm and an average reflectance of 2%.

Comparative Example 1

The coating layer was formed in the same manner as in Example 1, except that methyl ethyl ketone was used in an amount of 55 g and a silica particle was not contained in the coating composition.

Comparative Example 2

The coating layer was formed in the same manner as in Example 1, except that methyl ethyl ketone was used in an amount of 12 g and only a solution in which a silica particle S4 (d₁₀=12 nm, d₅₀=17 nm, d₉₀=21 nm, surface-modified with an acrylate silane coupling agent) was dispersed in MEK (hereinafter, referred to as S4 dispersion solution) was used in an amount of 112.5 g.

Comparative Example 3

The coating layer was formed in the same manner as in Example 1, except that methyl ethyl ketone was used in an amount of 35 g and only a S1 dispersion solution was contained in an amount of 110 g.

Comparative Example 4

The coating layer was formed in the same manner as in Example 1, except that a S3 dispersion solution was used in an amount of 125 g, a S4 dispersion solution in an amount of 25 g, and an additional methyl ethyl ketone solvent was not contained.

Comparative Example 5

Except for using a polyimide substrate (size: 20 cm×30 cm, thickness: 35 nm) having an elastic modulus value of 3.1 GPa as measured in accordance with ASTM D 882, the other steps were carried out in the same manner as in Example 1 to form a coating layer.

Comparative Example 6

Except for using a polyethylene terephthalate substrate (size: 20 cm×30 cm, thickness: 250 μm) having an elastic modulus value of 4.2 GPa as measured in accordance with ASTM D 882, the other steps were carried out in the same manner as in Example 1 to form a coating layer.

Comparative Example 7

Except for using 70 g of PS610 (manufactured by Miwon, Mw=5,400 g/mol, acrylate group equivalent weight=900 g/mol) as a 6-functional polyester acrylate-based binder instead of MU9800 and MU9020 in Comparative Example 3, the other steps were carried out in the same manner as in Comparative Example 3 to form a coating layer.

The main components of the coating layers of Examples 1 to 7 and Comparative Examples 1 to 7 are summarized Tables 1 and 2 below, respectively.

In Examples and Comparative Examples, the particle size distribution (d₁₀, d₅₀, d₉₀) of the inorganic fine particles was measured in the state of a dispersed solution using Malvern Zetasizer Nano-ZS 90 to determine a size distribution by number.

TABLE 1 Example Example Example Example Example Example Example 1 2 3 4 5 6 7 Acrylatebased TMPTA 30 30 30 20 30 30 30 binder MU9800 40 40 40 40 40 40 — (unit: g) MU9020 30 30 30 40 30 30 30 SC2152 — — — — — — 40 Inorganic S1 30 30 30 30 30 30 30 fine S2 15 25 — — 15 15 25 particles* S3 — — 15 30 — — — (unit: g) S4 — — — — — — — Substrate Thickness 35 μm 35 μm 35 μm 35 μm 35 μm 35 μm 35 μm and of substrate coating Elastic 6.0 GPa 6.0 GPa 6.0 GPa 6.0 GPa 4.2 GPa 7.6 GPa 6.0 GPa layer modulus of substrate Thickness  6 μm  6 μm  6 μm  6 μm  6 μm  6 μm  6 μm of coating layer Total 47 μm 47 μm 47 μm 47 μm 47 μm 47 μm 47 μm thickness

TABLE 2 Comparative Comparative Comparative Comparative Comparative Comparative Comparative Example Example Example Example Example Example Example 1 2 3 4 5 6 7 Acrylate TMPTA 30 30 30 30 30 30 30 based binder MU9800 40 40 40 40 40 40 — (unit: g) MU9020 30 30 30 30 30 30 — PS610 — — — — — — 70 Inorganic S1 — — 55 — 30 30 55 fine S2 — — — — 15 15 — particles* S3 — — — 50 — — — (unit: g) S4 — 45 — 10 — — — Substrate Thickness 35 μm 35 μm 35 μm 35 μm 35 μm 250 μm 35 μm and coating of layer substrate Elastic 6.0 GPa 6.0 GPa 6.0 GPa 6.0 GPa 3.1 GPa 4.2 GPa 6.0 GPa modulaus of subjstrate Thickness  6 μm  6 μm  6 μm  6 μm  6 μm  6 μm  6 μm of coating layer Total 47 μm 47 μm 47 μm 47 μm 47 μm 262 μm 47 μm thickness *In Table 1 and 2, the content of the inorganic fine particles is represented by the net weight of only the inorganic fine particles (S1 to S4) excluding the solvent according to the weight percentage of the inorgamic fine particles dispersed in the solvent.

Experimental Example

<Measurement Method>

1) Pencil Hardness

The maximum hardness without scratches was confirmed after moving the pencil back and forth three times at an angle of 45 degrees under a load of 750 g using a pencil hardness tester in accordance with standard JIS K5400-5-4.

2) Transmittance and Haze

The transmittance and haze were measured using a spectrophotometer (apparatus name: COH-400).

3) Bending Test

Each film was interposed and wound between cylindrical mandrels of various diameters and then the minimum diameter at which no cracks occurred was measured.

4) Bending Stability Test

FIG. 1 is a view schematically showing a method for performing a bending stability test of a film according to one embodiment of the present invention.

Each of the films of Examples and Comparative Examples was cut, but laser cutting was performed into a size of 80×140 mm so as to minimize fine cracks at the edge portions.

The laser cut film was placed on the fixing device, set so that the interval between the folded portions was 4 mm, and then allowed to stand at room temperature for 24 hours while both sides of the film being folded at 90 degrees to the bottom of the film. The film was then peeled off and the film was turned over so that the folded portion went downward. The □-shaped SUS structure was placed thereon and the film was fixed. The 3D image of the film shape was measured with a noncontact-type surface roughness measuring instrument (PLUTO 681, Dukin Co., Ltd., use of 605 nm laser, resolution 0.1 μm), and the maximum height of the height Z lifted from the bottom was measured as the bending stability property.

In addition, in order to measure the recovery of the films, the films in which the bending stability properties were measured were allowed to stand at room temperature for 1 hour.

The folded portion of the film was downwardly turned over. The □-shaped SUS structure was placed thereon and the film was fixed. The 3D image of the film shape was measured with a noncontact-type surface roughness measuring instrument (PLUTO 681, Dukin Co., Ltd., use of 605 nm laser, resolution 0.1 μm), and the maximum height of the height Z lifted from the bottom was measured and the change in the appearance of the folded portion were visually observed.

If Z is 0.1 mm or less and appearance change such as traces of folded parts is insufficient, it is shown as OK, and if Z exceeds 0.1 mm or a large number of traces remain on the folded portions, it is shown as NG.

The measurement results of the physical properties are shown in Tables 3 and 4 below.

TABLE 3 Example Example Example Example Example Example Example 1 2 3 4 5 6 7 Pencil hardness 7H 8H 7H 8H 6H 7H 6H Haze  0.4%  0.3%  0.4%  0.4%  0.4%  0.3%  0.4% Transmittance 91.9% 91.8% 92.0% 91.9% 91.9% 92.1% 91.7% Bending test   4 mm   4 mm   4 mm   4 mm   3 mm   4 mm   3 mm Bending stability 0.2 mm 0.2 mm 0.2 mm 0.2 mm 0.1 mm 0.2 mm 0.1 mm Recovery OK OK OK OK OK OK OK

TABLE 4 Comparative Comparative Comparative Comparative Comparative Comparative Comparative Example Example Example Example Example Example Example 1 2 3 4 5 6 7 Pencil 4H 5H 8H 5H 4H 6H 8H hardness Haze  0.2%  0.3%  0.4%  0.4%  0.3%  0.5%  0.3% Transmittance 92.1% 91.9% 91.8% 91.8% 92.1% 92.0% 92.0% Bending test   3 mm   4 mm 5 mm   4 mm   3 mm 20 mm 8 mm Bending 0.1 mm 0.2 mm Unmeasurable 0.3 mm 0.1 mm Unmeasurable Unmeasurable stability Recovery OK OK NG OK OK NG NG

Referring to Tables 3 and 4, the films of the present invention exhibited excellent characteristics in terms of each physical property, and particularly showed excellent stability in bending tests including high hardness.

On the other hand, the films of Comparative Examples had lowered pencil hardness or did not exhibit sufficient bending durability to be suitable for flexible films. 

What is claimed is:
 1. A flexible plastic film comprising: a substrate selected from the group consisting of polyimide (PI), polyimideamide, polyetherimide (PEI), polyethyleneterephtalate (PET), polyethylenenaphthalate (PEN), polyetheretherketone (PEEK), cyclic olefin polymer (COP), polyacrylate (PAC), polymethylmethacrylate (PMMA), and triacetylcellulose (TAC); and an ultraviolet-cured coating layer formed on at least one surface of the substrate, wherein the coating layer comprises a crosslinked copolymer of an acrylate-based binder and a urethane acrylate-based binder and inorganic fine particles having a bimodal particle size distribution including a first inorganic fine particle group having d₅₀ diameter of 20 to 35 nm and a second inorganic fine particle group having d₅₀ diameter of 40 to 130 nm, wherein the first inorganic fine particle group has d₁₀ diameter of 10 to 19 nm and d₉₀ diameter of 25 to 40 nm, and the second inorganic fine particle group has d₁₀ diameter of 25 to 110 nm and d₉₀ diameter of 60 to 150 nm, and wherein the flexible plastic film exhibits a pencil hardness of 6H or more under a load of 750 g, and and has properties such that the flexible plastic film does not lift by a height of more than 0.5 mm from a flat surface according to a bending stability test in which the flexible plastic film is folded 180° around a 4 mm rod for 24 hours at room temperature and is then spread on the flat surface.
 2. The flexible plastic film according to claim 1, wherein the substrate has an elastic modulus of 4 to 9 GPa as measured according to ASTM D882.
 3. The flexible plastic film according to claim 1, wherein the substrate has a thickness of 20 to 200 μm.
 4. The flexible plastic film according to claim 1, wherein the an ultraviolet-cured coating layer has a thickness of 3 to 20 μm.
 5. The flexible plastic film according to claim 1, wherein the acrylate-based binder is a 3- to 6-functional acrylate-based binder and wherein the urethane acrylate-based binder is a 7- to 20-functional urethane acrylate-based binder.
 6. The flexible plastic film according to claim 5, wherein the weight ratio between the 3- to 6-functional acrylate-based binder and the 7- to 20-functional urethane acrylate-based binder is 1:9 to 4:6.
 7. The flexible plastic film according to claim 5, wherein the an ultraviolet-cured coating layer includes the 3- to 6-functional acrylate-based binder in an amount of 10 to 50 parts by weight, the 7- to 20-functional urethane acrylate-based binder an amount of 40 to 70 parts by weight, the first inorganic fine particle group in an amount of 5 to 50 parts by weight and the second inorganic fine particle group in an amount of 5 to 50 parts by weight, based on 100 parts by weight of an ultraviolet-cured coating layer.
 8. The flexible plastic film according to claim 1, wherein the first inorganic fine particle group and the second inorganic fine particle group each is independently surface-modified with any one or more silane coupling agents selected from the group consisting of (meth)acrylsilane, methacryloxysilane, vinylsilane, epoxysilane, and mercaptosilane.
 9. The flexible plastic film according to claim 1, wherein the weight ratio between the first inorganic fine particle group and the second inorganic fine particle group is 9:1 to 3:7.
 10. The flexible plastic film according to claim 1, further comprising an antistatic layer or a low refractive index layer on the upper surface or the lower surface of the coating layer.
 11. The flexible plastic film according to claim 1, wherein the flexible plastic film does not crack when bent 180° around a 4 mm diameter mandrel. 